Product Description

Joaboa Tech Coating Series

JS Polymer Modified Cement Waterproofing Coating is a two-component polymer waterproof coating made of high quality polymer emulsion and cement as the main raw materials, added with a variety of inorganic materials and additives.

JS acrylic polymer modified cement based waterproofing coating has the advantages of excellent weather resistance, strong adhesion, high strength, non-toxic and tasteless, etc.

※   Material Features

1. Good Bonding Strength

JS polymer modified cementitious waterproofing coating can be applied on dry or wet base surface, with good adhesion.

2. Composite Use

JS polymer modified cement waterproofing can be used with a variety of other waterproof coatings or waterproofing membranes, suitable for different levels of waterproof engineering.

3. Strong Water Resistance

Compared with similar products, JS polymer modified cementitious coating has good water resistance and durable waterproof effect.

4. Environment-friendly

JS acrylic polymer modified cementitious coating does not pollute the environment and is harmless to human body. It can be used for waterproof engineering of drinking pool.

※   Scope of Application

1) JS acrylic polymer cementitious coating is applicable to inner and outer wall, kitchen, toilet, balcony, terrace, roof and other non-exposed waterproof works.

2) Suitable for basement, swimming pool, pool and other parts of the waterproof, seepage engineering.

※  Construction Requirments

1. Make sure substrates are leveled, firm, clean and no visual water on the surface. Any cracks should be repaired first. Internal & external corners need to camber.And dry substrates should be moistened.

2. If necessary, mix emulsion with water at the weight ratio of 1:1, then brush the mixture on the substrates.

3. Add cement into the J100 Coating slowly, stir the mixture evenly with electric mixer for 5 mins.

Proportioning of waterproofing coating: Weigh materials as emulsion/cement=1/1. 

4. Brush thinly for several times with scraper evenly. The next brushing of acrylic cementitious waterproofing coating should conduct after the prior becomes surface dry.

5. Application method with fiberglass mesh: generally, J100 acrylic polymer modified cementitious coating needs two times brushing. Place the fiberglassmesh after the first brushing, and keep it leveled. Do the second time brushing after the prior coating filmbecomes surface dry but not hard dry.

※  Construction Methods

JS Polymer Modified Cement Waterproofing Coating can use construction methods as below: brushing, roller coating, spraying, etc.

※  Packing Method

Professional loading method with wooden pallets to ensure the safety of J100 Polymer Cementitious Waterproof Coating during export.

※  Techinical Data Sheet of JS Polymer Cementitious Waterproofing Coating

※  Storage and Transport

1. JS polymer cement based waterproof coating is non-flammable and explosive material, which can be transported as general goods. During transportation, it should be protected from sun protection, frost protection, rain protection, extrusion and collision. Keep the package intact.

2. JS modified cement waterproofing shall be stored in a ventilated, dry and protected from direct sunlight.

3. JS polymer cement waterproofing should be stored in the warehouse at the temperature within 5℃-35℃, and the shelf life of the product is 6 months.

4. Products of different types and specifications should be stacked separately and should not be mixed.